Sample: As-received Cross-rolled Ti-4Al Alloy Ungroup Processes
Last Updated: 4 years ago Owner: Qianying Shi ID: 6777
Annealing Heat Treatment (1)
Settings
Temperature:
950 C
Cooling Type:
{ "name": "Water Quench", "value": "water_quench" }
Cooling Rate:
No value
Time:
6 h
Fractography (1)
Settings
Working Distance:
No value mm
Vertical Direction:
No value
Current:
No value
Voltage:
No value
Acquisition Time:
No value
Sample Tilt:
No value degress
Scan Size Height:
No value microns
Magnification:
No value
Step Size:
No value microns
Scan Size Width:
No value microns
Horizontal Direction:
No value
Files
Microstructure & Texture (1)
Settings
Magnification:
No value
Step Size:
No value microns
Working Distance:
No value mm
Sample Tilt:
No value degress
Current:
No value
Voltage:
No value
Vertical Direction:
No value
Horizontal Direction:
No value
Scan Size Height:
No value microns
Acquisition Time:
No value
Scan Size Width:
No value microns
Files
Receive Materials from Timet (1)
Settings
Supplier:
No value
Manufacturer:
Timet
Manufacturing Date:
No value
Production Method:
No value
Small Fatigue Crack Growth (1)
Settings
Resonating Frequency:
No value kHz
Stress Ratio:
-1
Test Environment:
Air
Calibration Constant:
No value
Test Temperature:
25 C
Amplifiers Count:
No value
Max Stress:
No value MPa
Power Control:
No value
Files
Tensile Test (1)
Settings
Test Rate:
10^-4/s
Gage Length:
25.4 mm
Control Mode:
{ "name": "Displacement", "value": "displacement" }
Force Type:
{ "name": "Hydraulic", "value": "hydraulic" }
Sample Geometry:
{ "name": "Cylindrical", "value": "cylindrical" }
Temperature:
25 C
Files
Ultrasonic Fatigue Lifetime (1)
Settings
Calibration Constant:
No value
Max Stress:
No value MPa
Stress Ratio:
-1
Test Temperature:
25 C
Test Environment:
Air
Resonating Frequency:
No value kHz
Power Control:
No value
Amplifiers Count:
No value